Typical Sieve Analysis
50 HPX | 65 HPX | 80 HPX | 85 HPX | 120 HPX | 150 HPX | 220 HPX | 60 HPA | 80 HPA | 100 HPA |
| |
|
|
|
|
|
Tyler Screen (micron) |
Percentage Retained |
|
32(500) |
1.0 |
|
35(425) |
16.0 |
|
42(355) |
37.0 |
|
48(300) |
29.0 |
|
60(250) |
15.0 |
|
65(212) |
2.0 |
|
80(180) |
|
|
100(150) |
|
|
115(125) |
|
|
150(106) |
|
|
170(90) |
|
|
200(75) |
|
|
250(63) |
|
|
270(53) |
|
|
325(45) |
| |
|
| 65 HPX |
|
Tyler Screen (Micron) |
Percentage Retained |
| 32 |
3.0 |
| 35 |
17.0 |
| 42 |
24.0 |
| 48 |
20.0 |
| 60 |
18.0 |
| 65 |
11.0 |
| 80 |
7.0 | |
| |
|
---------- top ^ |
| 80 HPX |
|
Tyler Screen (micron) |
Percentage Retained |
|
32(500) |
|
|
35(425) |
|
|
42(355) |
3.0 |
|
48(300) |
15.0 |
|
60(250) |
31.0 |
|
65(212) |
24.0 |
|
80(180) |
17.0 |
|
100(150) |
7.0 |
|
115(125) |
3.0 |
|
150(106) |
|
|
170(90) |
|
|
200(75) |
|
|
250(63) |
|
|
270(53) |
|
|
325(45) |
| |
|
|
|
|
Tyler Screen (Micron) |
Percentage Retained |
| 32(500) |
|
| 35(425) |
|
| 42(355) |
3.0 |
| 48(300) |
9.0 |
| 60(250) |
15.0 |
| 65(212) |
14.0 |
| 80(180) |
15.0 |
| 100(150) |
21.0 |
| 115(125) |
15.0 |
| 150(106) |
6.0 |
| 170(90) |
2.0 |
| 200(75) |
|
| 250(63) |
|
| 270(53) |
|
| 325(45) |
| |
| |
|
---------- top ^ |
|
|
|
Tyler Screen (micron) |
Percentage Retained |
|
32(500) |
|
|
35(425) |
|
|
42(355) |
|
|
48(300) |
|
|
60(250) |
|
|
65(212) |
2.0 |
|
80(180) |
11.0 |
|
100(150) |
30.0 |
|
115(125) |
28.0 |
|
150(106) |
16.0 |
|
170(90) |
7.0 |
|
200(75) |
6.0 |
|
250(63) |
|
|
270(53) |
|
|
325(45) |
| |
|
|
|
|
Tyler Screen (micron) |
Percentage Retained |
|
32(500) |
|
|
35(425) |
|
|
42(355) |
|
|
48(300) |
|
|
60(250) |
|
|
65(212) |
|
|
80(180) |
|
|
100(150) |
1.0 |
|
115(125) |
14.0 |
|
150(106) |
38.0 |
|
170(90) |
27.0 |
|
200(75) |
14.0 |
|
250(63) |
4.0 |
|
270(53) |
1.0 |
|
325(45) |
1.0 | |
| |
|
---------- top ^ |
|
|
|
Tyler Screen (micron) |
Percentage Retained |
| 32(500) |
|
| 35(425) |
|
| 42(355) |
|
| 48(300) |
|
| 60(250) |
|
| 65(212) |
|
| 80(180) |
|
| 100(150) |
|
| 115(125) |
5.0 |
| 150(106) |
18.0 |
| 170(90) |
24.0 |
| 200(75) |
25.0 |
| 250(63) |
18.0 |
| 270(53) |
7.0 |
| 325(45) |
3.0 | |
|
|
|
|
Tyler Screen (micron) |
Percentage Retained |
| 32(500) |
|
| 35(425) |
|
| 42(355) |
10.0 |
| 48(300) |
28.0 |
| 60(250) |
38.0 |
| 65(212) |
16.0 |
| 80(180) |
7.0 |
| 100(150) |
7.0 |
| 115(125) |
5.0 |
| 150(106) |
|
| 170(90) |
|
| 200(75) |
|
| 250(63) |
|
| 270(53) |
|
| 325(45) |
| |
| |
|
---------- top ^ |
|
|
|
Tyler Screen (micron) |
Percentage Retained |
|
32(500) |
|
|
35(425) |
|
|
42(355) |
|
|
48(300) |
7.0 |
|
60(250) |
38.0 |
|
65(212) |
30.0 |
|
80(180) |
20.0 |
|
100(150) |
5.0 |
|
115(125) |
|
|
150(106) |
|
|
170(90) |
|
|
200(75) |
|
|
250(63) |
|
|
270(53) |
|
|
325(45) |
| |
|
|
|
|
Tyler Screen (micron) |
Percentage Retained |
|
32(500) |
|
|
35(425) |
|
|
42(355) |
|
|
48(300) |
|
|
60(250) |
|
|
65(212) |
5.0 |
|
80(180) |
50.0 |
|
100(150) |
35.0 |
|
115(125) |
8.0 |
|
150(106) |
2.0 |
|
170(90) |
|
|
200(75) |
|
|
250(63) |
|
|
270(53) |
|
|
325(45) |
| |